1.1 This practice covers a test procedure for measuring ultrasonic velocities in materials with conventional ultrasonic pulse echo flaw detection equipment in which results are displayed in an A-scan display. This practice describes a method whereby unknown ultrasonic velocities in a material sample are determined by comparative measurements using a reference material whose ultrasonic velocities are accurately known.
1.2 This procedure is intended for solid materials 5 mm (0.2?in.) thick or greater. The surfaces normal to the direction of energy propagation shall be parallel to at least ±3°. Surface finish for velocity measurements shall be 3.2 µm (125 µin.) root-mean-square (rms) or smoother.
Note 1: Sound wave velocities are cited in this practice using the fundamental units of meters per second, with inches per second supplied for reference in many cases. For some calculations, it is convenient to think of velocities in units of millimeters per microsecond. While these units work nicely in the calculations, the more natural units were chosen for use in the tables in this practice. The values can be simply converted from m/s to mm/µs by moving the decimal point three places to the left, that is, 3500 m/s becomes 3.5 mm/µs.
1.3 Ultrasonic velocity measurements are useful for determining several important material properties. Young's modulus of elasticity, Poisson's ratio, acoustic impedance, and several other useful properties and coefficients can be calculated for solid materials with the ultrasonic velocities if the density is known (see Appendix X1).
1.4 More accurate results than those obtained using this method can be obtained with more specialized ultrasonic equipment, auxiliary equipment, and specialized techniques. Some of the supplemental techniques are described in Appendix X2. (Material contained in Appendix X2 is for informational purposes only.)
Note 2: Factors including techniques, equipment, types of material, and operator variables will result in variations in absolute velocity readings, sometimes by as much as ±5?%. Relative results with a single combination of the above factors can be expected to be much more accurate (probably within a 1?% tolerance).
1.5 Units—The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Rationale:
This practice covers a test procedure for measuring ultrasonic velocities in materials with conventional ultrasonic pulse echo flaw detection equipment in which results are displayed in an A-scan display, and describes a method whereby unknown ultrasonic velocities in a material sample are determined by comparative measurements using a reference material whose ultrasonic velocities are accurately known. The ultrasonic testing system that shall be used shall consist of the test instrument, search unit, couplant, and the standard reference blocks. The test procedure shall include both longitudinal and transverse wave velocity measurements, which should conform to the theoretical values of the parameters.
Significance and Use:
5.1 This practice describes a test procedure for the application of conventional ultrasonic methods to determine unknown ultrasonic velocities in a material sample by comparative measurements using a reference material whose ultrasonic velocities are accurately known.
5.2 Although not all methods described in this practice are applied equally or universally to all velocity measurements in different materials, it does provide flexibility and a basis for establishing contractual criteria between users, and may be used as a general guideline for preparing a detailed procedure or specification for a particular application.
5.3 This practice is directed towards the determination of longitudinal and shear wave velocities using the appropriate sound wave form. This practice also outlines methods to determine elastic modulus and can be applied in both contact and immersion mode.
Informations supplémentaires
| Auteur | American Society for Testing and Materials (ASTM International) |
|---|---|
| Comité | E07.06 - Committee E07 on Nondestructive Testing |
| Edité par | ASTM |
| Type de document | Norme |
| Thème | ,Non-destructive testing of metals |
| ICS | 77.040.20 : Essais non destructifs des métaux
|
| Nombre de pages | 14 |
| Remplace | ASTM E494-15 |
| Recueil | ASTM Volume 03.03 - Multi-User - Single-Site Online |
| Historique | ,,,, |
| Mot-clé | E494 |
| Bon de commande |
|