1.1 This specification covers methods to investigate the effectiveness of a material to beneficially change the properties of hydraulic cements when the material is incorporated during manufacture of the cement.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 The effect of additions in cement may markedly change properties other than those they are intended to modify. This specification is designed to test for such changes. Table 1 sets forth values for those properties of cement pastes and mortars that would permit a judgment of the changes effected by an addition. Likewise, Table 2 sets forth similar criteria for concrete. Certain additions may be found effective for more than one purpose as indicated in 3.1.4 and 3.1.5.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Rationale:
This specification covers methods to investigate the effectiveness of a material to beneficially change the properties of hydraulic cements when the material is interground with the clinker during manufacture of the cement. Cement, mortar, and concrete shall be tested and the individual grades shall conform to specified values of autoclave expansion, drying shrinkage, normal consistency, standard consistency, setting time, compressive strength, false set, water content, flexural strength, bond to steel, volume change, resistance to freezing and thawing, and bleeding. Accelerating addition, retarding addition, set-control addition, water-reducing addition, water-reducing and accelerating addition are detailed.
Informations supplémentaires
| Auteur | American Society for Testing and Materials (ASTM International) |
|---|---|
| Comité | C01.20 - Committee C01 on Cement |
| Edité par | ASTM |
| Type de document | Norme |
| Thème | ,Cement. Gypsum. Lime. Mortar |
| ICS | 91.100.10 : Ciment. Plâtre. Chaux. Mortier
|
| Nombre de pages | 5 |
| Remplace | ASTM C688-14 |
| Recueil | ASTM Volume 04.01 - Multi-User - Single-Site Online |
| Mot-clé | C688 |